API 5L X42 se yon bon kalite materyèl asye tiyo, sitou itilize pou manifakti lwil oliv ak gaz transmisyon tiyo.
Klas X42-PSL1 ERW tiyo asye kabòn Konpozisyon chimik (%)
| konpozisyon | C | Mn | P | S | Kr | Ni | Taks | Mouvman | B | Plis | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiyo san pwoblèm | Min | - | - | - | - | - | - | - | - | - | Nb+V+Ti Mwens pase oswa egal a 0.15 |
| Maks | 0.28 | 1.3 | 0.03 | 0.03 | 0.5 | 0.5 | 0.5 | 0.15 | 0.001 |
| konpozisyon | C | Mn | P | S | Kr | Ni | Cu | Mo | B | Plis | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiyo soude | Min | - | - | - | - | - | - | - | - | - | Nb+V+Ti Mwens pase oswa egal a 0.15 |
| Maks | 0.26 | 1.3 | 0.03 | 0.03 | 0.5 | 0.5 | 0.5 | 0.15 | 0.001 |
Klas X42-PSL1 tiyo liy san pwoblèm Pwopriyete mekanik
| Kalite | fòs rupture σb Mpa |
Pwen sede σs Mpa |
Elongasyon oswa elongasyon apre ka zo kase δ % |
|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | Pi gran pase oswa egal a 415 | Pi gran pase oswa egal a 290 | * |
Klas X42R-PSL2 Espiral submerged arc soude tiyo (SSAW) Konpozisyon chimik (%)
| konpozisyon | C | sizo | Mn | P | S | Kr | Ni | Taks | Mouvman | Tibèkil | V | Nòb | B | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | Min | - | - | - | - | - | - | - | - | - | - | - | - | - |
| Maks | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.3 | 0.3 | 0.5 | 0.15 | 0.04 | 0.06 | 0.05 | 0.001 |
Klas X42R-PSL2 Dwat kouti submerged arc soude tiyo (LSAW) Pwopriyete mekanik
| Kalite | Tanperati tès la | Fòs rupture σb Mpa |
Pwen sede σs Mpa |
Elongasyon oswa elongasyon apre ka zo kase δ % |
Enpak absòpsyon enèji KV2 J |
|---|---|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | 415~655 | 290~495 | * | ||
| OD mwens pase oswa egal a 20 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>20~30 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>30~84 | 0 degre | Pi gran pase oswa egal a 40 |
Klas X42N-PSL2 Rezistans soude tiyo (ERW) Konpozisyon chimik (%)
| Konpozisyon | C | sizo | Mn | P | S | Kr | Ni | Taks | Mouvman | Tibèkil | V | Nòb | B | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | Min | - | - | - | - | - | - | - | - | - | - | - | - | - |
| Maks | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.3 | 0.3 | 0.5 | 0.15 | 0.04 | 0.06 | 0.05 | 0.001 |
Tiyo klas X42N-PSL2 pou likid ki ka pran dife Pwopriyete mekanik
| Kalite | Tanperati tès la | Fòs rupture σb Mpa |
Pwen sede σs Mpa |
Elongasyon oswa elongasyon apre ka zo kase δ % |
Enpak absòpsyon enèji KV2 J |
|---|---|---|---|---|---|
|
Tiyo san pwoblèm, tiyo soude |
415~655 | 290~495 | * | ||
| OD mwens pase oswa egal a 20 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>20~30 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>30~84 | 0 degre | Pi gran pase oswa egal a 40 |
Klas X42Q-PSL2 tiyo san pwoblèm pou gaz natirèl konpozisyon chimik (%)
| Konpozisyon | C | sizo | Mn | P | S | Kr | Ni | Taks | Mouvman | Tibèkil | V | Nòb | B | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | Min | - | - | - | - | - | - | - | - | - | - | - | - | - |
| Maks | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.3 | 0.3 | 0.5 | 0.15 | 0.04 | 0.05 | 0.05 | 0.001 |
Klas X42Q-PSL2 lwil oliv ak gaz tiyo Pwopriyete mekanik
| Kalite | Tanperati tès la | Fòs rupture σb Mpa |
Pwen sede σs Mpa |
Elongasyon oswa elongasyon apre ka zo kase δ % |
Enpak absòpsyon enèji KV2 J |
|---|---|---|---|---|---|
| Tiyo san pwoblèm, tiyo soude | 415~655 | 290~495 | * | ||
| OD mwens pase oswa egal a 20 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>20~30 | 0 degre | Pi gran pase oswa egal a 27 | |||
| OD>30~84 | 0 degre | Pi gran pase oswa egal a 40 |
GNEE API 5L X42 Pipeline pou vann